Brass
Brass is a copper alloy in which the main alloying element is zinc. The generic term “brass” covers a wide range of materials suitable for many different types of applications.
Characteristics of Brass
- Good corrosion resistance
- Good machinability & formability
- Good conductivity
- Toughness at all temperatures
- Good spark resistance
- Low magnetic permeability
Gilding brass
Contain 10 - 20% zinc and are used for architectural metal work, paper making, jewellery strips, and applications requiring suitability for brazing and enameling.
Cartridge brass
Contain 30% zinc, have the maximum ductility of the copper-zinc range and are used for deep drawing.
Common brass
Contains 36% zinc and is the most usual composition used for brass sheet.
Free machining brass
Contains 39% zinc and is the standard alloy against which machinability of other alloys has been judged.
BRASS SHEET
|
Length |
Width |
Thickness |
kg/sheet |
Finish |
Temper |
|
1800 mm |
900 mm |
0.500 mm |
6.910 kg/sheet |
POLISHED |
1/2 Hard |
|
2000 mm |
1000 mm |
0.700 mm |
12.00 kg/sheet |
POLISHED |
1/2 Hard |
|
2000 mm |
1000 mm |
0.900 mm |
15.40 kg/sheet |
POLISHED |
1/2 Hard |
|
2000 mm |
1000 mm |
1.200 mm |
20.50 kg/sheet |
POLISHED |
1/2 Hard |
|
2000 mm |
1000 mm |
1.600 mm |
26.60 kg/sheet |
POLISHED |
1/2 Hard |
|
2000 mm |
1000 mm |
2.000 mm |
33.78 kg/sheet |
POLISHED |
1/2 Hard |
BRASS PLATE
|
Length |
Width |
Thickness |
kg/sheet |
Finish |
Temper |
|
1800 mm |
900.0 mm |
5.000 mm |
69.100 kg/sheet |
Mill Finish |
1/2 Hard |
|
1800 mm |
900.0 mm |
6.000 mm |
82.910 kg/sheet |
Mill Finish |
1/2 Hard |
|
1000 mm |
600.0 mm |
20.000 mm |
104.00 kg/sheet |
Mill Finish |
1/2 Hard |
|
1000 mm |
600.0 mm |
25.000 mm |
130.00 kg/sheet |
Mill Finish |
1/2 Hard |
|
2000 mm |
1000 mm |
10.000 mm |
173.00 kg/sheet |
Mill Finish |
1/2 Hard |